1.COMPOSITION AND PRESENTATION

Battery separator surfacing mat is mainly used as substrate for lead-acid battery speparator plate. The compound separator plate made of C-SAB mat with PVC or rubber coating has the advantages of better mechanic stength and vibration resistance, low mass resistivity, high porosity and large capacity. The battery fixed up with this type of separator plates possesses stronger starting power and longer lifetime so that it has become a tend to replace the traditonal separator plate with this novel compound plate made of fiberglass and rubber/PVC.The property data of the battery fixed up with C-SAB mat plate meet all the specifications specified in japanese industrial standard JIS –C2202 Fiberglass Mat for lead-acid storage battey. At the same time, the compound plate made of C-SAB mat is also in conformity with the specifications detailed in JB 3385-91, a mechanic industry standard of the Peope’s Republic of china.

2. PROPERTIES & APPLICATION

 Properties:

Low content of deoxidized KMnO4 orgnic substance and impurity, High absorption  capacity, Low DC mass resistivty, Good acid resistance, Uniform thidkness, Smooth surface, Proper stiffness.                              

Application :

Battery separator surfacing mat is mainly used as substrate for lead-acid battery speparator plate.

3.MAIN TECHNICAL CHARACTERISTICS

Item	Style
	C-SAB0.30	C-SAB0.40	C-SAB0.50	C-SAB0.60	C-SAB0.80
Area Weight   (g/㎡)	35	45		58	78
Binder Content  (%)	16	16	16	15	14
Thickness  (mm)	0.33	0.43	0.54	0.64	0.85
Acid resistance / 72hrs  (%)	＜3.00	＜3.00	＜3.00	＜3.00	＜3.00
Tensile Strength MD  (N/5cm)	≥60	≥80	≥100	≥120	≥160
Wetting time  (s)	＜100	＜25	＜10	＜10	＜10
Acid resistance / 15min  (%)	＜2.00	＜2.00	＜2.00	＜2.00	＜2.00
Width×length  (m×m)	1.0×2500	1.0×2500	1.0×2500	1.0×2000	1.0×1500
Roll Diameter  (M)	＜1.17	＜1.17	＜1.17	＜1.17	＜1.17
Paper Core Internal Dia  (cm)	15	15	15	15	15